<sub id="1pfbv"><var id="1pfbv"></var></sub>

<sub id="1pfbv"></sub><sub id="1pfbv"><dfn id="1pfbv"></dfn></sub>

<thead id="1pfbv"><var id="1pfbv"><output id="1pfbv"></output></var></thead>
<form id="1pfbv"></form><address id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></address>
<sub id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></sub>

<sub id="1pfbv"></sub>

<address id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></address><sub id="1pfbv"><var id="1pfbv"></var></sub>
<form id="1pfbv"></form>

<sub id="1pfbv"><dfn id="1pfbv"></dfn></sub>

<sub id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></sub>
      <address id="1pfbv"></address>
      <address id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></address>

        <thead id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></thead>

        <sub id="1pfbv"><dfn id="1pfbv"><ins id="1pfbv"></ins></dfn></sub>
        <address id="1pfbv"><dfn id="1pfbv"></dfn></address>

        028-85466065
        技術支持
        常見問題
        您現在的位置:網站首頁 > 常見問題

        牙科硬質鈷鉻合金鑄件出現鑄造不全的原因有哪些?

        1、鑄圈焙燒不透,造成鑄造時鑄圈溫度過低,金屬熔化后進入鑄圈流通不暢。鑄造鈷鉻類合金,鑄圈焙燒時,300℃前慢慢升溫,在300℃和600℃時各停留30min,焙燒到最高溫度時再保溫30min以上。(最高溫度請參照烤瓷包埋料廠家說明)。

        2、合金熔金不完全,會造成金屬流通不暢,鑄道堵塞。處理辦法:牙科硬質鈷鉻合金在加熱熔化時,金屬表面形成一層明顯的氧化膜,且氧化膜破膜形成鏡面時,為最佳鑄造時機。

        3、鑄道設計與安插不當:如鑄道與鑄件之間形成銳角,使合金流通不暢,分鑄道設計過多等。(根據實際情況應做相應的調整。)